China Clear Unsaturated Polyester Resin for Translucent FRP Sheet

Product Description

We have reisn for 1: Hand lay-up General purpose, 2: Flame retardant, 3: Chemical resistance 4: Food grade5. Spray up, 6. For boat7. Button8. For pultrusion and RTM 9. For FW pipe 10. For paint 11. For translucent panel 12. Cultured marble 13. SMC/BMC 14, Hobas

We have an Isopthalic resin, non-promoted and low viscosity polyester resin for pipes, tanks and other applications submitted to chemicals manufactured by spray-up, hand lay-up and filament winding. This resin is also recommended for food, medicines, cosmetics and potable water storage. We export this resin to South America.

Technical Data Sheet:

1: Hand lay-up General purpose
Code	Type		25ºC Pa.s Viscosity		Min gel time		% Non-Volatile		Mpa Tensile strength		% Elongation		Mpa Flexural Strength		HDT	Application
JL-189	PA		0.25-0.45		10-22		59-65		60		4.0		100		57	Water resistance, for boat.CCS
JL191	PA		0.25-0.45		9-17		61-67		55		1.8		110		66	Translucent, general FRP purpose
JL-191RS	PA		0.25-0.45		9-17		61-67		60		3.5		114		70	For FRP product, general purpose
JL-196	PA		0.60-1.20		9.1-18.9		64-70		76		2.0		120		72	Flexibility, high strength, CCS
JL-580	IPA		0.40-0.70		10-20		66-70		15		68		10		67	Flexibilizer or flexible resin, with other resins
JL-1032	PA		0.25-0.65		15-23		15-23		60		2.0		105		67	Good mechanical property, for bus,boat, CCS approval
JL-22	PA		0.34-0.38		16-22		16-22		62		2.3		108		65	Pre-promoted, thixotropy and low shrinkage
JL-2068	PA		0.20-0.40		11-25		11-25		58		1.5		110		100	Hot water resistance and high HDT,for bathtub
JL-10070	PA		0.30-0.34		8-18		8-18		65		2.0		115		68	Low viscosity, rapid wetting reinforcement for high strength FRP products.
2. For FW pipe
Code		Type		25ºC Pa.s Viscosity		Min gel time		% Non-Volatile		Mpa Tensile strength		% Elongation		Mpa Flexural Strength	HDT		Application
JL-102		IPA		0.20-0.40		7-13		51-57		64		2.0		115	105		For lining, good flexibility, chemical resistance and high HDT, for water supply and drainage pipe, petroleum pipe and chemical industry pipe, tank
JL-191FW		PA		0.30-0.50		15-30		60-67		65		2.5		120	81		For structure, flexible and good mechanical property for FW pipe and tanks
JL-1900		PA		0.30-0.40		30-35		62-68		65		2.5		120	70		For structure, low PET and crack resistance
JL-196SPFW		PA		0.30-0.50		8.5-17.5		60-68		70		2.0		120	70		For lining, to make FW pipe and tanks, food grade, CNH approval
JL-20820		IPA		0.22-0.48		9-21		58-64		72		3.2		120	86		For lining, to make FW pipe and tanks, food grade, CNH approval
JL-10600		PA		0.20-0.26		5-12		55-61		68		2.7		138	81		For structure and HOBAS pipe
JL-503831		PA		0.20-0.40		5.5-12.5		56-62		11		76					High elongation for lining and HOBAS pipe, food grade, CNH approval