Conveyor Belt System Repair Cold Vulcanizing Solution Ts801
Conveyor belt cold vulcanizing cement TS2000, 1kg/set(with adhesive and hardener). Can replace Tiptop SC2000Product Application:Conveyor belt cold vulcanizing cement TS2000, two-component adhesive,it's the ideal conveyor belt damage repair cement when bonding rubber to rubber,rubber to fabric, r......
Send Inquiry
Product Description
Conveyor belt cold vulcanizing cement TS2000, 1kg/set(with adhesive and hardener). Can replace Tiptop SC2000
Product Application:
Conveyor belt cold vulcanizing cement TS2000, two-component adhesive,it's the ideal conveyor belt damage repair cement when bonding rubber to rubber,rubber to fabric, rubber to metal and fabric to fabric bonding, or used in corrosion and wear protection applications for conveyor belt applications.
How to use:
1, Surface treatment: Deburring the parts to be bonded. Clean and dry the parts.
2, Mix: Pour the B-part into A-part directly and stir them quickly. Then, pour the mixed adhesive to the parts.
3, Curing: Curing time is 2 hours at room temperature. After 24 hours, it can get to highest bonding strength.
Technical data sheet:
Packing:
1kg/set, 10sets/carton;
Product Application:
Conveyor belt cold vulcanizing cement TS2000, two-component adhesive,it's the ideal conveyor belt damage repair cement when bonding rubber to rubber,rubber to fabric, rubber to metal and fabric to fabric bonding, or used in corrosion and wear protection applications for conveyor belt applications.
Product Features:
1 Non-flammable.
2 Fast speed of solidifying(curing time can be 2 hours), high intension, anticorrosion, resistance to aging in normal temperature.
3.Easy operation and low cost.
How to use:
1, Surface treatment: Deburring the parts to be bonded. Clean and dry the parts.
2, Mix: Pour the B-part into A-part directly and stir them quickly. Then, pour the mixed adhesive to the parts.
3, Curing: Curing time is 2 hours at room temperature. After 24 hours, it can get to highest bonding strength.
Technical data sheet:
| Part No. | Color | Appearance | Density(g/cm³) | Peel strength(N/cm) GB/T2791-1995 | Mix ratio | Operating time(min) | Curing time | Heat resistant(°C) |
| TS2000 | Black | Liquid | 0.9-1.3 | 120 | A:B=100:5 | 20-40 | 2 hours | 100 |
Packing:
1kg/set, 10sets/carton;